GB/T 713 07Cr2AlMoR steel plate, also written as 07Cr2AlMoR pressure vessel steel plate, GB713 07Cr2AlMoR, Cr-Al-Mo vessel plate, is a low-carbon Cr-Al-Mo alloy pressure vessel plate under GB/T 713 / GB/T 713.2, typically N+T (temper ≥680°C), with about 260 MPa min yield (6–36 mm) and tensile 420-580 MPa; rare-earth additions may be agreed. Gangsteel (HENAN GANG IRON AND STEEL) produces and exports 07Cr2AlMoR plates cut to size with MTC for Cr-Al-Mo corrosion/elevated-temperature service.
Data source: Per GB/T 713 / GB/T 713.2-2023 (Steel plate, sheet and strip for pressure equipments — Part 2: Non-alloy and alloy steel with specified temperature properties; buyers still search “GB/T 713”). Official mill/certificate grade is 07Cr2AlMoR. Verify the contracted edition and purchase-order supplements before ordering.
| Element | C | Si | Mn | P | S | Cr |
|---|---|---|---|---|---|---|
| 07Cr2AlMoR, % | 0.09 max | 0.20-0.50 | 0.40-0.90 | 0.020 max | 0.010 max | 1.60-2.20 |
| Element | Mo | Al | Cu | Ni | RE | — |
|---|---|---|---|---|---|---|
| 07Cr2AlMoR, % | 0.30-0.50 | 0.30-0.60 | 0.30 max | 0.30 max | optional | — |
Per GB/T 713.2 heat analysis. Al + Cr support oxidation/corrosion resistance; RE optional when specified.
| Thickness | Yield ReL, min | Tensile Rm | Elongation A, min | Impact KV2 |
|---|---|---|---|---|
| 6–36 mm | 260 MPa | 420-580 MPa | 19% | 20°C, ≥47 J |
| >36–60 mm | 250 MPa | 410-570 MPa | 19% | 20°C, ≥47 J |
Per GB/T 713.2. N+T; temper ≥680°C.
Normalized + tempered (temper ≥680°C). Optional RE, PWHT simulation, UT and 3.1/3.2 MTC.
Commonly 6–60 mm (confirm mill max), width 1500-4000 mm, length 6000-18000 mm.
Cr-Al-Mo pressure equipment needing improved oxidation/corrosion resistance with moderate strength.
| Standard | Comparable grade (approximate) |
|---|---|
| GB/T 713 | 07Cr2AlMoR |
| ASTM/ASME | ASTM A387 / SA387 / A387 Grade 12 (approx. for Cr-Mo class) |
| EN 10028-2 | 13CrMo4-5 (approx. for 1Cr-Mo class) |
| Related GB/T 713 | Q245R | Q345R | Q370R | Q420R | Q460R |
Equivalents are engineering references only. Dual certification requires the stricter combined limits on the PO and MTC.
It is a Cr-Al-Mo boiler and pressure vessel steel under GB/T 713 / GB/T 713.2. a low-carbon Cr-Al-Mo alloy pressure vessel plate under GB/T 713 / GB/T 713.2, typically N+T (temper ≥680°C), with about 260 MPa min yield (6–36 mm) and tensile 420-580 MPa; rare-earth additions may be agreed. Gangsteel lists the official mill/certificate grade as 07Cr2AlMoR. See the full GB/T 713 07Cr2AlMoR page for chemistry and mechanical tables.
About 260 MPa min at 6–36 mm; ~250 MPa at 36–60 mm. Typical tensile bands are shown in the mechanical properties table on this page; confirm the contracted GB/T 713.2 edition before design.
20°C standard (typically ≥47 J). Always state the required Charpy temperature and energy on the purchase order.
Normalized + tempered (temper ≥680°C). Optional RE, PWHT simulation, UT and 3.1/3.2 MTC.
07Cr2AlMoR is in the Cr-Al-Mo alloy family under GB/T 713.2. Related alloy grades: 15CrMoR / 14Cr1MoR / 12Cr2Mo1R / 12Cr1MoVR / 12Cr2Mo1VR / 18MnMoNbR / 13MnNiMoR. Carbon workhorses remain Q345R / Q245R.
They are approximate engineering counterparts only. Compare with ASTM A387 / SA387 and EN 10028-2 13CrMo4-5. Dual certification requires the stricter combined limits.
EN 10204 3.1 as standard; 3.2 with third-party inspection when ordered. MTC lists heat analysis, mechanical tests, delivery condition and any optional UT / Z / HIC / elevated-temperature results.
Commonly 6–60 mm (confirm mill max), width 1500-4000 mm, length 6000-18000 mm. Browse the GB/T 713 hub for the full grade list.