WYJ030-2006                             16MnR(HIC)-A

1. applicable scope

The technology conditions apply to 8 mm thickness-120 mm in the wet acidic environment of MnR summer use 16 cracking (HIC)-A steel plate.

2. Of the steel plate size and shape, weight, allow deviation

The steel plate size and shape, weight, deviation should be allowed to meet the provisions of GB6654-1996 standard.

3. Chemical composition

The chemical composition of steel should be in accordance with table 1.

Table 1

* Ca value for reference only, do not make acceptance conditions, Ca O content analysis can be used instead of finished product value melting analysis value.

* * carbon equivalent (CE) computation formula is as follows: CE = C + Mn / 6

* * * S content of the target of 0.002%

4. Delivery status: normalized

5. Mechanical properties and process performance

5.1 sample simulation of heat treatment after welding after stretching, impact, bending test results should comply with the provisions of the table 2. Quartile 24 mm steel plate thickness, and its thickness direction performance also should be consistent with the GB/T5313-1985 in the provisions of the Z35 level.

5.2 brinell hardness

Steel should be finished by piece brinell hardness testing, brinell hardness value ≤200 HB

Table 2