1, the technology conditions of the ASME SA299 / SA299M equivalent to the latest version, suitable for welding boiler and other pressure vessel USES the steel plate.
2, the steel plate size and shape, weight and deviation should be allowed to meet the provisions of SA20 standard.
3, technical requirements
3.1 chemical composition
The chemical composition of the steel plate (melting analysis) shall conform to the provisions of ASME SA299 steel plate, see table 1.
Table 1 wt%
composition |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Nb |
Cu |
Al |
Melting analysis |
≤0.28 |
0.15 ~0.40 |
0.90~1.50 |
≤0.020 |
≤0.010 |
≤0.25 |
≤0.25 |
≤0.10 |
≤0.02 |
≤0.25 |
≥0.020 |
Produce analysis |
≤0.28 |
0.13~0.45 |
0.84~1.62 |
≤0.025 |
≤0.015 |
≤0.25 |
≤0.25 |
≤0.11 |
≤0.03 |
≤0.25 |
≥0.020 |
Note :Ni+Cr+Mo+Cu+V+Nb≤0.80%。
3.2 delivery status: the steel plate to normalizedstate delivery. Sample simulation after welding heat treatment system: 610 ±5 ℃, heat preservation 8 hours, more than 300 ℃,≤150 ℃cooling speed/h, 300 ℃below are not limit. PWHT size simulation for: long quartile 3 T x width quartile 3 T ×T (T-thickness).
3.3 mechanics and process performance
3.3.1 PWHT should comply with the provisions of the table 2.
table2
thick (mm) |
σs (Mpa) |
σb (Mpa) |
δ5gauge length 50mm(%) |
0℃impact
J |
180° cold bend
|
8-25 |
≥290 |
515~655 |
≥19 |
≥27 |
d=4a |
≥25 |
≥275 |
Note: (1) the table 2 impact energy for three samples of the arithmetic mean, allow one of the single value less than 27 J, but shall not be less than 20 J.
(2) less than 12 mm thickness of steel, do not do the impact test.
3.3.2normalizeddelivery the tensile properties of high temperature steel plate to table 3.
Table 3
Test temperature℃ |
σ0.2 Mpa |
σb Mpa |
350 |
≥205 |
≥480 |
GANGSTEEL Galvanized Coil Steel Stock List and Price 2016-02-25
The tension was high as Gregoire Parenty and Martin Lindqvist took the stage to announce the winner of the 2015
EN10025-5 S355J0WP,S355J2WP,S355J0W,S355J2W steel plate
DIN 17155 HII | HII steel plate DIN standard HII pressure vessel steel has now been superseded with the Euro No