EN10028-6 P460Q|P460Q STEEL PLATE
EN10028-6 P460Q standard specification forWeldable fine grain steels, quenched and tempered .
P460Q Grade has a good weldable and used in high temperature equipment and pressure vessel.
P…Q means the -20 degree and the impact energy is 27J
P…QH means the -20 temperature quality and the impact energy is 27J
P…QL1 means the -40 temperature quality and the impact energy is 27J
P…QL2 means the -60 temperature quality and the impact energy is 27J
Supplementary Technology: HIC Test | NACE MR0175 | Z15 | Z25 | Z35 |
Thickness: 6MM to 300MM,
Width: 1500mm to 4050mm,
Length: 3000mm to 15000mm
Gangsteelis specialized in supplying EN10028-6 steel plate in P460Q. For more information of P460Q steel plates, please check them in following:
|
P460Q Chemical Composition |
|||||||
|
Grade |
The Element Max (%) |
||||||
|
C |
Si |
Mn |
P |
S |
N |
B |
|
|
P460Q |
0.18 |
0.50 |
1.70 |
0.025 |
0.015 |
0.015 |
0.005 |
|
Mo |
Cu |
Nb |
Ni |
Ti |
V |
Zr |
|
|
0.50 |
0.3 |
0.05 |
0.5 |
0.03 |
0.06 |
0.05 |
|
Carbon Equivalent: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%
|
Grade |
P460Q Mechanical Property |
|||
|
Thickness |
Yield |
Tensile |
Elongation |
|
|
P460Q |
mm |
Min Mpa |
Mpa |
Min % |
|
6-50 |
460 |
550-720 |
19% |
|
|
50-100 |
440 |
550-720 |
19% |
|
|
100-150 |
400 |
500-670 |
19% |
|
Shipbuilding steel plate| Alloy steel plates| High strength plate| Carbon steel plate| Stainless steel plate
If you need more stock steel plates in pressure vessel steel plate, please click warehouse sizes.
Related Grade: P460QH | P460QL1 |P460Q
EN10028-2 P355GH for High-Strength Low-Alloy Columbium-Vanadium Structural Steel EN10025-2 S355J2 Structural St
We export A240 304L Stainless Coil 2B, NO.1 No.4 surface, the thickness 0.1mm to 3mm, 3mm to 22mm, Mother mill
ASTM A516 GR 70 equivalent materials is such as ASME SA516 GR 70, EN 10028 P355GH, and BS1501 224-490 A & B, sh
The astm a516 gr 70 yield strength of 260 MPa ensures structural integrity in high-pressure applications, such