EN 10025 2 S235JR Steel Equivalent ASTM A283 Grade C

EN 10025-2 S235JR is a European standard non-alloy structural steel grade with a minimum yield strength of 235 MPa, known for its good weldability, machinability, and suitability for general construction. Its equivalent in ASTM standards is A283 Grade C, a low-carbon steel plate with similar moderate strength and properties for structural and pressure vessel applications.

As a leading Chinese manufacturer and exporter, Gangsteel produces high-quality plates equivalent to S235JR under asme sa 283/sa 283m, offering reliable alternatives for global projects in buildings, bridges, and machinery.

 

Overview of EN 10025-2 S235JR and ASTM A283 Grade C

EN 10025-2 S235JR is a hot-rolled structural steel used in non-critical applications like buildings and bridges, with good impact resistance at room temperature (JR designation). ASTM A283 Grade C is a low and intermediate tensile strength carbon steel plate for similar structural purposes, often used in tanks and general fabrication. Both have low carbon content for excellent weldability, making them interchangeable in many cases. Gangsteel's asme sa 283/sa 283m plates provide equivalent performance, including grades like sa 283 grade a steel plate, sa 283 grade b steel plate, sa 283 grade c steel plate, and sa 283 grade d steel plate for versatile structural needs.

The table below compares S235JR and A283 Grade C:

Property

EN 10025-2 S235JR

ASTM A283 Grade C

Standard

EN 10025-2

ASTM A283/A283M

Yield Strength (min, MPa/ksi)

235 / 34

205 / 30

Tensile Strength (MPa/ksi)

360-510 / 52-74

380-515 / 55-75

Elongation (min, %)

26

22

Applications

Structural components, welding

Structural, tanks, fabrication

Weldability

Excellent

Excellent

 

Chemical Composition Comparison

S235JR and A283 Grade C have similar low-carbon compositions for good weldability, with minor differences in manganese and carbon limits. Below is a table of typical compositions (in weight %, maximum unless specified):

Element

S235JR

A283 Grade C

C (Carbon)

0.17

0.24

Mn (Manganese)

1.40

0.90

P (Phosphorus)

0.045

0.035

S (Sulfur)

0.045

0.040

Si (Silicon)

-

0.40

Cu (Copper)

-

0.20 (min if specified)

Gangsteel's sa 283 grade c steel plate offers a similar low-carbon profile for equivalent performance.

 

Mechanical Properties Comparison

S235JR and A283 Grade C have overlapping mechanical properties, with S235JR providing slightly higher yield strength. The table below details typical values:

Property

S235JR

A283 Grade C

Yield Strength (min, MPa/ksi)

235 / 34

205 / 30

Tensile Strength (MPa/ksi)

360-510 / 52-74

380-515 / 55-75

Elongation (min, %)

26

22

Impact Test

27J at 20°C (JR)

Not required

Gangsteel's asme sa 283/sa 283m plates match these for structural reliability.

 

Applications and Interchangeability

Both are used in construction for beams, plates, and welded structures, with good corrosion resistance. They are often interchangeable, though A283 Grade C may suit pressure vessels better. Gangsteel's plates support this with certifications.

 

FAQ

  • What is the closest ASTM equivalent to S235JR?ASTM A283 Grade C, with similar yield strength and applications.
  • Is A36 also equivalent to S235JR?Yes, A36 is another close match with 250 MPa yield.
  • How do S235JR and A283 Grade C differ?S235JR has impact testing; A283 Grade C focuses on tensile properties.
  • Can S235JR and A283 Grade C be interchanged?Yes, in most general structural applications.
  • Where can I buy S235JR or A283 Grade C equivalent plates?Gangsteel offers compliant plates; contact for asme sa 283/sa 283m.

 