Gangsteel – China's Leading Mill-Direct Supplier & Exporter of S355ML Material Properties EN 10025-4 Steel Plates
Gangsteel is the expert supplier for S355ML material properties EN 10025-4 steel plates, providing comprehensive data on this thermomechanically rolled (TMCP) fine-grain structural steel to facilitate precise engineering and compliance worldwide. As defined in EN 10025-4:2004 (2019 revision), S355ML offers a minimum yield strength of 355 MPa, exceptional weldability (CEV ≤0.39), and low-temperature toughness (≥27 J at –50 °C longitudinal), making it indispensable for high-performance applications.
We stock over 5,000 tons of S355ML plates—thicknesses 6–200 mm, widths 1500–4200 mm, lengths up to 18 meters—produced by leading mills like HBIS and Shougang with full PED 2014/68/EU and CPR 305/2011 certification. Every plate includes detailed EN 10204-3.1/3.2 MTCs outlining material properties, plus third-party verifications from DNV-GL, ABS, Lloyd's Register, Bureau Veritas, CCS, RINA, KR, TÜV, or SGS.
Material properties of S355ML—encompassing chemical composition, mechanical strength, density (7.85 g/cm³), hardness (140-180 HBW), and impact resistance—are key to its success in weight-optimized designs under Eurocode 3, reducing sections 15-20% versus S355J2 while ensuring fatigue life >10^7 cycles at 160 MPa. Z25/Z35 through-thickness and 100% UT EN 10160 S2/E2 are standard for flaw detection. Gangsteel equips you with property data for FEA modeling, weld procedure qualification (WPS), and certification, with fast delivery (3–7 days globally) and services like cutting, beveling, drilling, rolling, and priming. Delve into our en 10025 4 High Strength Structural Steel portfolio for the complete series. For a foundational overview, explore S355ML Meaning EN 10025-4 Structural Steel Supplier.
The material properties of S355ML under EN 10025-4:2004 (2019) define its identity as a thermomechanically rolled (TMCP) weldable fine-grain structural steel engineered for high-strength, low-temperature demands. "S" signifies structural suitability for load-bearing; "355" the nominal minimum yield strength of 355 MPa (transverse, ≤16 mm thick); "M" the TMCP delivery, involving controlled hot rolling (900-1100 °C) and accelerated cooling (20-40 °C/s) to form a refined ferrite-bainite microstructure; and "L" enhanced Charpy V-notch impact of ≥27 J at –50 °C longitudinally, per EN ISO 148-1.
TMCP's material properties—low residual stresses (<100 MPa), fine grains (ASTM 8-10), and CEV ≤0.39—yield superior weldability (no preheat to 80 mm), ductility (≥22% elongation), and isotropy, outperforming normalized S355NL (EN 10025-3) by 20-30% in distortion resistance. Density 7.85 g/cm³ ensures accurate mass calculations for buoyancy in offshore FEA, while hardness 140-180 HBW supports machinability (feed rates 0.2-0.3 mm/rev). Microalloying (Nb ≤0.05%, V ≤0.10%, Ti ≤0.05%) pins boundaries for toughness, with P/S ≤0.025/0.020% minimizing brittleness.
These properties enable S355ML in Eurocode 3 fatigue designs (S-N >10^7 cycles at 160 MPa) and DNV-OS-B101 offshore, where KV prevents cleavage (ductile ≥50% fibrous). Gangsteel verifies properties via spectrographic/UT, providing data for CTOD (>0.4 mm at –40 °C) and KIc (>140 MPa√m). For chemical specifics, see S355ML Chemical Composition EN 10025-4 Supplier; for mechanical, S355ML Mechanical Properties EN 10025-4 Plate Supplier.
|
Element |
Ladle Max (%) |
Product Deviation (%) |
Typical Actual (%) – Gangsteel Stock |
Role in Material Properties |
|---|---|---|---|---|
|
C |
0.14 |
+0.02 |
0.09–0.12 |
Low C for weld ductility; base for yield |
|
Si |
0.50 |
+0.05 |
0.20–0.40 |
Deoxidizer; stabilizes ferrite for toughness |
|
Mn |
1.60 |
+0.10 |
1.20–1.50 |
Strengthens solid solution; elongation aid |
|
P |
0.025 |
+0.005 |
≤0.018 |
Min P for grain boundary cohesion |
|
S |
0.020 |
+0.005 |
≤0.015 |
Low S for inclusion-free KV |
|
Nb |
0.05 |
+0.01 |
0.02–0.04 |
Pins grains for fine structure/elongation |
|
V |
0.10 |
+0.02 |
0.04–0.08 |
Precipitates for hardening/toughness |
|
Al min |
0.020 |
+0.030 (total) |
0.025–0.045 |
Deoxidizes for clean matrix/hardness control |
|
Ti |
0.05 |
+0.03 |
0.01–0.03 |
Nitride former for isotropy |
|
Cr |
0.30 |
+0.05 |
0.10–0.25 |
Hardenability for Rm range |
|
Ni |
0.50 |
+0.05 |
0.20–0.40 |
Low-temp transition for KV |
|
Mo |
0.10 |
+0.03 |
≤0.05 |
HAZ stability |
|
Cu |
0.55 |
+0.03 |
0.20–0.35 |
Deoxidizer; minor corrosion resistance |
|
N |
0.015 |
+0.003 |
≤0.012 |
Low for nitride-free properties |
|
CEV max |
0.39 |
N/A |
0.32–0.38 |
Weld index; overall ductility key |
CEV = C + Mn/6 + (Cr+Mo+V)/5 + (Ni+Cu)/15. Equivs match. Full: S355ML Chemical Composition EN 10025-4 Supplier.
|
Thickness (mm) |
ReH min (MPa) |
Rm (MPa) |
A5 min (%) |
KV min (J, long. –50 °C) |
|---|---|---|---|---|
|
≤16 |
355 |
470–630 |
22 |
27 |
|
16<t≤40 |
345 |
470–630 |
22 |
27 |
|
40<t≤63 |
335 |
470–630 |
22 |
27 |
|
63<t≤80 |
325 |
470–630 |
22 |
27 |
|
80<t≤100 |
315 |
470–630 |
22 |
27 |
|
100<t≤120 |
305 |
450–610 |
22 |
27 |
|
120<t≤150 |
295 |
450–610 |
22 |
27 |
|
150<t≤200 |
285–295* |
450–610 |
22 |
27 |
*Agreement >150 mm; Gangsteel 295 MPa to 180 mm. Hardness 140-180 HBW; density 7.85 g/cm³. Curves: S355ML Mechanical Properties EN 10025-4 Plate Supplier.
S355ML properties vs. family.
|
Property/Grade |
S275M/ML |
S355M |
S355ML |
S420M/ML |
|---|---|---|---|---|
|
Yield (MPa, ≤16 mm) |
275 |
355 |
355 |
420 |
|
Impact Temp (Long.) |
-20°C (M)/-50°C (ML) |
-20°C |
-50°C |
-20°C (M)/-50°C (ML) |
|
Min KV (J) |
40/-20°C; 27/-50°C |
40/-20°C |
27/-50°C |
40/-20°C; 27/-50°C |
|
CEV Max |
0.38 |
0.39 |
0.39 |
0.43 |
|
Elong. A5 Min (%) |
24 |
22 |
22 |
19 |
|
Tensile (MPa) |
370-530 |
470-630 |
470-630 |
520-680 |
|
No-Preheat (mm) |
100 |
80 |
80 |
60 |
|
Wt Save vs S355J2 |
5-10% |
15-20% |
15-20% |
20-25% |
|
Cost + vs S355J2 (USD/t) |
+40-60 |
+80-120 |
+100-150 |
+150-200 |
|
Density (g/cm³) |
7.85 |
7.85 |
7.85 |
7.85 |
|
Apps |
Light frames |
Bridges |
Offshore |
Cranes |
|
Gangsteel Stock |
High |
V. High |
Highest |
Med |
S355ML balanced properties; vs S355M, –50 °C KV; vs S275ML, 30% stronger; vs S420ML, ductility. See S355M vs S355ML EN 10025-4 Steel Plate Comparison Supplier.
Properties equivs match S355ML.
|
Standard |
Equivalent Grade |
Key Match Notes |
Typical Use Case |
|---|---|---|---|
|
ASTM/ASME |
A572 Gr.50 + Z35 |
Yield 345 MPa; properties align |
U.S. properties calc |
|
JIS G 3106 |
SM490A |
Rm 490 MPa; ductility same |
Japanese properties FEA |
|
GB/T 1591 |
Q355E |
Low-temp properties |
China-EN properties |
|
API 2W |
Grade 50 |
Offshore properties |
Low-temp platforms |
|
EN 10025-6 |
S355QL |
QT properties; S355ML cheaper |
Heavy properties loads |
Indicative; TMCP properties better HAZ. Dual-cert. Full: S355ML Equivalent Material EN 10025-4 Plate Supplier.
Properties for Eurocode 3, 18% less steel.
Notes: Interpass 150°C; ER50-2. FEA properties input, 2% hardening. Eco: 97% recycle, 20% CO2 save. Gangsteel V-50°, UT S4.
To 92+ countries: Rotterdam 7 days.
Q1: S355ML vs S355M properties difference?
A: Impact temp: S355ML –50 °C ≥27 J for cold (offshore/Arctic); S355M –20 °C ≥40 J for temperate. Yield/chem/elong/density same—ML for < –20 °C (DNV-OS-B101). Gangsteel stocks both with full properties MTCs.
Q2: Welding preheat for S355ML properties?
A: None to 80 mm (CEV 0.32-0.38); low-H E7018 H4. Thicker: 70-120 °C (EN ISO 13916). TMCP low stress preserves properties; saves 50 °C vs J2; CET per heat WPS.
Q3: S355ML for pressure vessels properties?
A: Yes, PED III (EN 13445); derate >63 mm. UT S3/E3; RT opt seams. Properties aid fracture (KIc >140 MPa√m); cost-effective vs QT; dual ASME/EN.
Q4: S355ML vs S355J2 properties price?
A: +100-140 USD/t for TMCP/-50 °C properties; offset 15-20% thinner + 25% fatigue. FOB 700-800 USD/t (25 mm); vol 10-15% discount.
Q5: Z35 in S355ML properties?
A: Z25 std; Z35 stocked (≥35% RA EN 10164 Cl.3) tension; +15-25 USD/t. Properties Norsok M-120 welds; density neutral.
Q6: ASTM equiv for S355ML properties?
A: A572 Gr.50 + Z35; yield 345 MPa, properties align –50 °C KV add. A633 Gr.C normalized; TMCP HAZ better. Dual-cert stocked.
Q7: Custom S355ML lead time properties?
A: Stock 1-3 days; processed 2-5 days; mill 3-5 weeks. 95% OTIF; air <10 MT 24-48 hrs; properties verified MTC.
For S355ML properties plates, quote now.
Email: admin@gangsteel.com WhatsApp/WeChat/Mobile: +86 135 9887 9167 Website: https://gangsteel.net/
Gangsteel—Properties Perfected, Projects Powered.
ASTM A516 GR 70 equivalent materials is such as ASME SA516 GR 70, EN 10028 P355GH, and BS1501 224-490 A & B, sh
we supply high-quality A516 Gr 70 steel plate for pressure vessel applications and other standards like ASTM A2
EN10028-2 P355GH for High-Strength Low-Alloy Columbium-Vanadium Structural Steel EN10025-2 S355J2 Structural St
We export A240 304L Stainless Coil 2B, NO.1 No.4 surface, the thickness 0.1mm to 3mm, 3mm to 22mm, Mother mill