Gangsteel – China's Leading Mill-Direct Supplier & Exporter of S460ML Mechanical Properties EN 10025-4 Data Sheet Steel Plates
Gangsteel is your definitive source for S460ML mechanical properties EN 10025-4 data sheet steel plates, providing downloadable, heat-specific data sheets with verified mechanical, chemical, and physical properties for precise engineering and compliance. As a thermomechanically rolled (TMCP) weldable fine-grain structural steel under EN 10025-4:2004 (2019 revision), S460ML's mechanical properties—minimum yield strength of 460 MPa, tensile range 540-720 MPa, elongation ≥17%, and low-temperature toughness ≥27 J at –50 °C longitudinal—make it the benchmark for maximum-strength, low-temperature structural applications. We stock over 5,000 tons of S460ML plates in thicknesses 6–200 mm, widths 1500–4200 mm, and lengths up to 18 meters, produced by premium mills like HBIS and Shougang with full PED 2014/68/EU and CPR 305/2011 certification. Each plate includes EN 10204-3.1/3.2 MTCs with full data sheet values, third-party inspections from DNV-GL, ABS, Lloyd's Register, Bureau Veritas, CCS, RINA, KR, TÜV, or SGS, Z25/Z35 through-thickness, and 100% UT EN 10160 S2/E2 testing.
S460ML data sheets from Gangsteel include spectrographic chemistry, tensile/yield/elongation per EN ISO 6892-1, Charpy V-notch per EN ISO 148-1 (sub-size for thick plates), hardness (HBW), density (7.85 g/cm³), and optional CTOD/KIc for fracture mechanics. CEV ≤0.48 ensures preheat-free welding to 80 mm. Fast 3–7 day delivery and processing (cutting, beveling, drilling, rolling, priming). Download sample data sheet or request heat-specific PDF. Explore our en 10025 4 High Strength Structural Steel series. For grade overview, S460ML Meaning EN 10025-4 Structural Steel Supplier.
The S460ML data sheet under EN 10025-4:2004 (2019) is the official technical document detailing all verified mechanical properties of this TMCP weldable fine-grain structural steel, where "S" means structural, "460" nominal yield 460 MPa (transverse ≤16 mm), "M" TMCP delivery (900-1100 °C rolling + 20-40 °C/s cooling), "L" enhanced –50 °C ≥27 J KV (EN ISO 148-1). Data sheets include ladle/product chemistry, mechanicals (yield, tensile, elongation, impact), physicals (density, hardness), and optional extras (Z-quality, CTOD).
TMCP's mechanical properties—low residual stress (<100 MPa), fine grains (ASTM 8-10), and CEV ≤0.48—yield superior weldability (no preheat to 80 mm), ductility (≥17% elongation), and fatigue life (>10^7 cycles at 180 MPa). Data sheets verify ReH 460 MPa min (actual 470-500 MPa typical), Rm 540-720 MPa, and KV per EN ISO 148-1 (10x10x55 mm, sub-size >40 mm). Density 7.85 g/cm³ and hardness 160-210 HBW support FEA (bilinear 2% hardening) and machining (0.2-0.3 mm/rev feeds).
S460ML mechanical properties enable 25-30% thinner sections than S355J2 under Eurocode 3, with partial factor γM0 = 1.0. Gangsteel data sheets are heat-traceable, supporting DNV-OS-B101 or AASHTO with CTOD (>0.4 mm) and KIc (>150 MPa√m at –40 °C). For chemical basis, S460ML Chemical Composition EN 10025-4 Supplier; mechanical, S460ML Mechanical Properties EN 10025-4 Plate Supplier.
|
Element |
Ladle Max (%) |
Product Deviation (%) |
Typical Actual (%) – Gangsteel Stock |
Role in Mechanical Properties |
|---|---|---|---|---|
|
C |
0.16 |
+0.02 |
0.10–0.14 |
Low C for weld ductility |
|
Si |
0.60 |
+0.05 |
0.20–0.50 |
Deoxidizer |
|
Mn |
1.70 |
+0.10 |
1.20–1.60 |
Strength for ReH 460 MPa |
|
P |
0.025 |
+0.005 |
≤0.018 |
Min P for toughness |
|
S |
0.020 |
+0.005 |
≤0.015 |
Low S for inclusion-free KV |
|
Nb |
0.05 |
+0.01 |
0.02–0.04 |
Pins grains for elongation |
|
V |
0.12 |
+0.02 |
0.05–0.10 |
Precipitates for Rm range |
|
Al min |
0.020 |
+0.030 (total) |
0.025–0.045 |
Deoxidizes for clean matrix |
|
Ti |
0.05 |
+0.03 |
0.01–0.03 |
Nitride for isotropy |
|
Cr |
0.30 |
+0.05 |
0.10–0.25 |
Controlled hardenability |
|
Ni |
0.80 |
+0.05 |
0.30–0.60 |
–50 °C transition |
|
Mo |
0.20 |
+0.03 |
≤0.10 |
HAZ stability |
|
Cu |
0.55 |
+0.03 |
0.20–0.40 |
Deoxidizer |
|
N |
0.025 |
+0.003 |
≤0.012 |
Low for properties |
|
CEV max |
0.48 |
N/A |
0.42–0.46 |
Weld index for ductility |
CEV = C + Mn/6 + (Cr+Mo+V)/5 + (Ni+Cu)/15. Equivs match. Full: S460ML Chemical Composition EN 10025-4 Supplier.
|
Thickness (mm) |
ReH min (MPa) |
Rm (MPa) |
A5 min (%) |
KV min (J, long. –50 °C) |
|---|---|---|---|---|
|
≤16 |
460 |
540–720 |
17 |
27 |
|
16<t≤40 |
440 |
540–720 |
17 |
27 |
|
40<t≤63 |
430 |
540–720 |
17 |
27 |
|
63<t≤80 |
410 |
540–720 |
17 |
27 |
|
80<t≤100 |
400 |
540–720 |
17 |
27 |
|
100<t≤120 |
385 |
530–710 |
17 |
27 |
|
120<t≤150 |
370 |
530–710 |
17 |
27 |
|
150<t≤200 |
350–380* |
530–710 |
17 |
27 |
*Agreement >150 mm; Gangsteel 380 MPa to 180 mm. Hardness 160-210 HBW; density 7.85 g/cm³. Curves: S460ML Mechanical Properties EN 10025-4 Plate Supplier.
S460ML properties vs. family.
|
Property/Grade |
S275M/ML |
S355M |
S460M |
S460ML |
S500M/ML |
|---|---|---|---|---|---|
|
Yield (MPa, ≤16 mm) |
275 |
355 |
460 |
460 |
500 |
|
Impact Temp (Long.) |
-20°C (M)/-50°C (ML) |
-20°C |
-20°C |
-50°C |
-20°C (M)/-50°C (ML) |
|
Min KV (J) |
40/-20°C; 27/-50°C |
40/-20°C |
40/-20°C |
27/-50°C |
40/-20°C; 27/-50°C |
|
CEV Max |
0.38 |
0.39 |
0.48 |
0.48 |
0.51 |
|
Elong. A5 Min (%) |
24 |
22 |
17 |
17 |
17 |
|
Tensile (MPa) |
370-530 |
470-630 |
540-720 |
540-720 |
570-720 |
|
No-Preheat (mm) |
100 |
80 |
80 |
80 |
60 |
|
Wt Save vs S355J2 |
5-10% |
15-20% |
25-30% |
25-30% |
30-35% |
|
Cost + vs S355J2 (USD/t) |
+40-60 |
+80-120 |
+140-180 |
+160-220 |
+200-250 |
|
Density (g/cm³) |
7.85 |
7.85 |
7.85 |
7.85 |
7.85 |
|
Apps |
Light frames |
Bridges |
Heavy structures |
Offshore |
Ultra-heavy |
|
Gangsteel Stock |
High |
V. High |
High |
Highest |
Limited |
S460ML balanced high strength/low-temp; vs S355ML, 30% higher yield; vs S460M, –50 °C KV; vs S500ML, better ductility/weldability. See S460M vs S460ML EN 10025-4 Impact Comparison Supplier.
Properties equivs.
|
Standard |
Equivalent Grade |
Key Match Notes |
Typical Use Case |
|---|---|---|---|
|
ASTM/ASME |
A913 Gr.65 + Z35 |
Yield 450 MPa; properties align |
U.S. properties calc |
|
JIS G 3106 |
SM570 |
Rm 570 MPa; ductility same |
Japanese properties FEA |
|
GB/T 1591 |
Q460E |
Low-temp properties |
China-EN properties |
|
API 2W |
Grade 60 |
Offshore properties |
Properties platforms |
|
EN 10025-6 |
S460QL |
QT properties; S460ML cheaper |
Heavy properties loads |
Indicative; TMCP properties better HAZ. Dual-cert. Full: S460ML Equivalent Material EN 10025-4 Plate Supplier.
Properties for Eurocode 3, 25-30% less steel.
Notes: Interpass 150°C; ER50-2. FEA properties input, 2% hardening. Eco: 97% recycle, 20% CO2 save. Gangsteel V-50°, UT S4. For weld properties, S355ML/NL Weldability EN 10025-4 Fine Grain Supplier; data S355ML Data Sheet EN 10025-4 Steel Properties Supplier.
To 92+ countries: Rotterdam 6 days. For specs, S460ML Specification EN 10025-4 Steel Plate Supplier; comparison S460ML vs S460M EN 10025-4 Impact Comparison Supplier.
Q1: S460ML mechanical properties exact value?
A: Yield 460 MPa min ≤16 mm, derating to 350 MPa at 150-200 mm (transverse). Actual Gangsteel 470-510 MPa typical; EN ISO 6892-1 tested. Key for Eurocode 3 allowable stress (f_y = ReH/γ_M0, γ_M0=1.0).
Q2: S460M vs S460ML properties difference?
A: Impact temp: S460M –20 °C ≥40 J for temperate (bridges/machinery); S460ML –50 °C ≥27 J for cold (offshore/Arctic). Yield/chem/elong/density same—ML for < –20 °C (DNV-OS-B101). Gangsteel stocks both with properties MTCs.
Q3: Welding preheat for S460ML properties?
A: None to 80 mm (CEV 0.42-0.46); low-H E7018 H4. Thicker: 75-120 °C (EN ISO 13916). TMCP low stress preserves properties; saves 50 °C vs J2; CET per heat WPS.
Q4: S460ML for pressure vessels properties?
A: Yes, PED III (EN 13445); derate >63 mm. UT S3/E3; RT opt seams. Properties aid fracture (KIc >150 MPa√m); cost-effective vs QT; dual ASME/EN.
Q5: Z35 in S460ML properties?
A: Z25 std; Z35 stocked (≥35% RA EN 10164 Cl.3) tension; +20-40 USD/t. Properties Norsok M-120 welds; density neutral.
Q6: ASTM equiv for S460ML properties?
A: A913 Gr.65 + Z35; yield 450 MPa, properties align –50 °C KV add. A871 Gr.65 normalized; TMCP HAZ better. Dual-cert stocked.
Q7: Custom S460ML lead time properties?
A: Stock 1-3 days; processed 2-5 days; mill 3-5 weeks. 95% OTIF; air <10 MT 24-48 hrs; properties verified MTC.
For S460ML properties plates, quote now.
Email: admin@gangsteel.com
ASTM A516 GR 70 equivalent materials is such as ASME SA516 GR 70, EN 10028 P355GH, and BS1501 224-490 A & B, sh
we supply high-quality A516 Gr 70 steel plate for pressure vessel applications and other standards like ASTM A2
EN10028-2 P355GH for High-Strength Low-Alloy Columbium-Vanadium Structural Steel EN10025-2 S355J2 Structural St
We export A240 304L Stainless Coil 2B, NO.1 No.4 surface, the thickness 0.1mm to 3mm, 3mm to 22mm, Mother mill